Put Titanium Technology to Work for You

Field tests of two Cat 793 Haul Trucks lined at a Utah copper mine alongside 4 competitors 500 BHN Wear Plates found that after 24 months of service, or 12,725 hours the REGOL 450 TC trucks had worn approx. 1/8″ at the worst point. This projects a 40,000 hour wear life on these trucks which is a 100% improvement over any other 500 Brinell wear plate previously tested at this mine. The same wear life improvement has been realized in haul trucks, chutes, and conveyor parts at several other mines. These field test results are a real testament to titanium technology. For additional test results, contact us.

Independent lab tests support what field tests prove, REGOL 450 TC is the most cost effective and long lasting wear plate. A DSRW test done to ASTM G65 Procedure B (2000 revs.) 1/2″ thick sample yields these results:

Air Hardening Steel
425 BHN AR Q & T
REGOL 450 TC
Hardness Weight Loss (g)
475 BHN
418 BHN
434 BHN
Weight Loss (g)AFS 50-70 Sand
0.587
0.653
0.444/td>
Weight Loss (g) Flattery Sand
0.167/0.167
0.159/0.161
0.123/0.120

Stock Sizes: 96″ x 288″
Average Plate Hardness: 450 BHN
Titanium HV Hardness: 3200
Tests 1/2″ Thick Material: 1/4″• 3/8″• 1/2″• 3/4″• 1″• 1-1/4 • 1-1/2″• 2″• 2-1/2″
Yield: 181,000
Tensile: 211,000
Charpy Impacts @ 32 deg. = 18 ft./lbs.

Improved abrasion resistance is achieved from the carbide matrix and the martensite developed by a special heat treating process. Nickel, Moly., Boron and other alloying elements are also added to enhance abrasion resistant properties.


澳洲8最新开奖号码

Carbon
.29
Silicon
.34
Manganese
.69
Phosphate
.007
Sulfer
.001
Chromium
.93